Red Travertine |
 |
|
|
 |
Physical, Mechanical and Technological
Specifications
|
|
|
| Hardness |
(Mohs) : |
4 |
|
|
|
| Unit Volume Weight |
(gr./cm3) : |
2,5 |
|
|
|
| Density |
(gr./cm3) : |
2,72 |
|
|
|
| Water absorption at atmospheire pressure, |
by weight t (%) : |
1 |
|
|
|
|
by volume (%) : |
2,3 |
|
|
|
| Water absorption at boiling water, |
by weight t (%) : |
1,2 |
|
|
|
|
by volume (%) : |
3 |
|
|
|
| Porosity |
(%) : |
2,3 |
|
|
|
| Compressive strength |
(Kgf/cm2) : |
570 |
|
|
|
| Compressive strength after freezing |
(Kgf/cm2) : |
582 |
|
|
|
| Strength to blow |
(Kgf/cm2) : |
11 |
|
|
|
| Strength to bending |
(Kgf/cm2) : |
108 |
|
|
|
| Modules of Elasticity |
(Kgf/cm2) : |
5,38x104 |
|
|
|
| Ratio of fuliness |
(%) : |
91,9 |
|
|
|
| Degree of pores |
(%) : |
8,1 |
|
|
|
| Average Abrasion Strenght |
(cm3/50 cm2) : |
28,7 |
|
|
|
| Average Tensile Strenght |
(Kgf/cm2) : |
41 |
|
|
|
| CHEMICAL ANALYSIS |
% |
|
|
|
|
SiO2 |
0,26 |
|
|
|
|
Fe2O3 |
0,32 |
|
|
|
|
CaO |
54,55 |
|
|
|
|
MgO |
0,31 |
|
|
|
|
|
 |